Three-Dimensional Modeling of Rust Peaks at the Steel-Concrete Interface and Prediction of Cover Cracking

JIANG Ce; ZHANG Xiaogang; ZHAO Xiaoye; XU Pinggui

doi:10.3724/j.gyjzG24111501

Volume 56 Issue 4

Apr. 2026

Turn off MathJax

Article Contents

Article Navigation > INDUSTRIAL CONSTRUCTION > 2026 > 56(4): 309-318

JIANG Ce, ZHANG Xiaogang, ZHAO Xiaoye, XU Pinggui. Three-Dimensional Modeling of Rust Peaks at the Steel-Concrete Interface and Prediction of Cover Cracking[J]. INDUSTRIAL CONSTRUCTION, 2026, 56(4): 309-318. doi: 10.3724/j.gyjzG24111501

Citation:

JIANG Ce, ZHANG Xiaogang, ZHAO Xiaoye, XU Pinggui. Three-Dimensional Modeling of Rust Peaks at the Steel-Concrete Interface and Prediction of Cover Cracking[J]. INDUSTRIAL CONSTRUCTION, 2026, 56(4): 309-318. doi: 10.3724/j.gyjzG24111501

Citation:

PDF( 2086 KB)

Three-Dimensional Modeling of Rust Peaks at the Steel-Concrete Interface and Prediction of Cover Cracking

doi: 10.3724/j.gyjzG24111501

College of Civil and Transportation Engineering, Shenzhen University, Shenzhen 518061, China

Received Date: 2024-11-15
Available Online: 2026-06-06
Publish Date: 2026-04-20

Abstract

Abstract

Rebar corrosion is a leading cause of degradation in reinforced concrete （RC） structures， particularly in coastal environments. This study investigated the corrosion-induced cracking mechanism of concrete cover， focusing on the localized accumulation of corrosion products （rust peaks） at the steel-concrete interface due to inherent defects. Micro-computed tomography （μCT） was employed to perform a non-destructive， three-dimensional analysis of rust peaks forming at the steel-concrete interface. A three-dimensional rust peak fitting model based on a two-dimensional Gaussian function was proposed， and its accuracy was verified with experimental data. Based on this model， the relations between rust peaks and natural interface defects were examined， and a corrosion-induced cracking model for the cover was established. The findings revealed that the crack width increased significantly with the growth of rust peak height， and specimens with thinner concrete cover were more prone to developing distinct cracks. The model demonstrated high prediction accuracy in laboratory testing， with most prediction errors remaining within 15%. These results provide theoretical support for understanding structural degradation induced by rebar corrosion in engineering practice， although their applicability in complex environments still requires further verification.
- rebar corrosion,
- cover cracking,
- μCT,
- three-dimensional rust peak model,
- durability assessment

FullText(HTML)

References(44)

References

[1]	陈华鹏，刘昌雨，江钰，等. 钢筋混凝土结构锈蚀开裂模型研究［J］. 铁道学报，2023，45（10）：180-188.
[2]	刘一凡，缪志伟，申晨，等. 基于蒙特卡罗法的不均匀锈蚀钢筋力学性能评估［J］. 吉林大学学报（工学版），2024，54（4）：1007-1015.
[3]	LEPORACE-GUIMIL B，CONFORTI A，ZERBINO R，et al. Chloride-induced corrosion in reinforced concrete and fiber reinforced concrete elements under tensile service loads［J］. Cement & Concrete Composites，2021，124：104245.
[4]	孙佳，金祖权，秦一琦. 钢筋非均匀锈蚀与混凝土开裂试验及数值模拟［J］. 建筑材料学报，2024，27（4）：309-319.
[5]	HONG S X，QIN S F，DONG P，et al. Quantification of rust penetration profile in reinforced concrete deduced by inverse modeling［J］. Cement & Concrete Composites，2020，111：103622.
[6]	ROSSI E，POLDER R，COPUROGLU O，et al. The influence of defects at the steel/concrete interface for chloride-induced pitting corrosion of naturally-deteriorated 20-years-old specimens studied through X-ray Computed Tomography［J］. Construction and Building Materials，2020，235：117474.
[7]	BERNACHY-BARBE F，SAYARI T，DEWYNTER-MARTY V，et al. Using X-ray microtomography to study the initiation of chloride-induced reinforcement corrosion in cracked concrete［J］. Construction and Building Materials，2020，259：119574.
[8]	郑少强，陈业强，刘荣桂，等. 海洋环境下混凝土结构耐久性寿命的概率分析［J］. 工业建筑，2023，53（5）：165-173.
[9]	SHI J J，MING J，ZHANG Y M，et al. Corrosion products and corrosion-induced cracks of low-alloy steel and low-carbon steel in concrete［J］. Cement & Concrete Composites，2018，88：121-129.
[10]	BHARGAVA K，GHOSH A K，MORI Y，et al. Modeling of time to corrosion-induced cover cracking in reinforced concrete structures［J］. Cement and Concrete Research，2005，35（11）：2203-2218.
[11]	CARE S，NGUYEN Q T，L'HOSTIS V，et al. Mechanical properties of the rust layer induced by impressed current method in reinforced mortar［J］. Cement and Concrete Research，2008，38（8/ 9）：1079-1091.
[12]	MAADDAWY T EL，SOUDKI K. A model for prediction of time from corrosion initiation to corrosion cracking［J］. Cement & Concrete Composites，2007，29（3）：168-175.
[13]	JANG B S，OH B H. Effects of non-uniform corrosion on the cracking and service life of reinforced concrete structures［J］. Cement and Concrete Research，2010，40（9）：1441-1450.
[14]	LUO G，ZHANG K，ZHU W J，et al. Effect of non-uniform corrosion on the cracking propagation of the RC specimens［J］. Construction and Building Materials，2021，270：121460.
[15]	XU Y D，SONG Y F. Chemical-mechanical transformation of the expansion effect for nonuniform steel corrosion and its application in predicting the concrete cover cracking time［J］. Cement & Concrete Composites，2022，127：104376.
[16]	ZHAO Y X，ZHANG X W，DING H J，et al. Non-uniform distribution of a corrosion layer at a steel/concrete interface described by a Gaussian model［J］. Corrosion Science，2016，112：1-12.
[17]	GUZMAN S，GALVEZ J C. Modelling of concrete cover cracking due to non-uniform corrosion of reinforcing steel［J］. Construction and Building Materials，2017，155：1063-1071.
[18]	YUAN Y S，JI Y S. Modeling corroded section configuration of steel bar in concrete structure［J］. Construction and Building Materials，2009，23（6）：2461-2466.
[19]	MALUMBELA G，ALEXANDER M，MOYO P. Model for cover cracking of RC beams due to partial surface steel corrosion［J］. Construction and Building Materials，2011，25（2）：987-991.
[20]	DU X L，JIN L，ZHANG R B. Modeling the cracking of cover concrete due to non-uniform corrosion of reinforcement［J］. Corrosion Science，2014，89：189-202.
[21]	ZHAO Y X，HU B Y，YU J，et al. Non-uniform distribution of rust layer around steel bar in concrete［J］. Corrosion Science，2011，53（12）：4300-4308.
[22]	YE H L，JIN N G，FU C Q，et al. Rust distribution and corrosion-induced cracking patterns of corner located rebar in concrete cover［J］. Construction and Building Materials，2017，156：684-691.
[23]	XI X，YANG S T，LI C Q. A non-uniform corrosion model and meso-scale fracture modelling of concrete［J］. Cement and Concrete Research，2018，108：87-102.
[24]	王娟，管巧艳，孔宇田，等. 界面初始缺陷对混凝土单轴抗拉强度的影响［J］. 水利水电科技进展，2016，36（5）：46-49.
[25]	ZHANG X G，ZUO G Q，MEMON S A，et al. Effects of initial defects within mortar cover on corrosion of steel and cracking of cover using X-ray computed tomography［J］. Construction and Building Materials，2019，223：265-277.
[26]	ZHANG W L，FRANCOIS R，CAI Y X，et al. Influence of artificial cracks and interfacial defects on the corrosion behavior of steel in concrete during corrosion initiation under a chloride environment［J］. Construction and Building Materials，2020，253：119165.
[27]	YU L W，FRANCOIS R，DANG V H，et al. Development of chloride-induced corrosion in pre-cracked RC beams under sustained loading：Effect of load-induced cracks，concrete cover，and exposure conditions［J］. Cement and Concrete Research，2015，67：246-258.
[28]	ZHANG W L，YU L W，FRANCOIS R. Influence of top-casting-induced defects on the corrosion of the compressive reinforcement of naturally corroded beams under sustained loading［J］. Construction and Building Materials，2019，229：116912.
[29]	CHEN F J，LI C Q，BAJI H，et al. Effect of design parameters on microstructure of steel-concrete interface in reinforced concrete［J］. Cement and Concrete Research，2019，119：1-10.
[30]	HE S H，HE J Y，GUO X C，et al. Detection of CFRP-concrete interfacial defects by using electrical measurement［J］. Composite Structures，2022，295：115843.
[31]	ZHAO Y X，YU J，HU B Y，et al. Crack shape and rust distribution in corrosion-induced cracking concrete［J］. Corrosion Science，2012，55：385-393.
[32]	WANG X Y，DONG S F，ASHOUR A，et al. Bond of nanoinclusions reinforced concrete with old concrete：Strength，reinforcing mechanisms and prediction model［J］. Construction and Building Materials，2021，283：122741.
[33]	YU S，JIN H. Modeling of the corrosion-induced crack in concrete contained transverse crack subject to chloride ion penetration［J］. Construction and Building Materials，2020，258：119645.
[34]	LIU Z H，CHEN X D，WU P，et al. Investigation on micro-structure of self-compacting concrete modi fi ed by recycled grinded tire rubber based on X-ray computed tomography technology［J］. Journal of Cleaner Production，2021，290：125838.
[35]	ALHUSAIN M，AL-MAYAH A. Three dimensional imaging of reinforcement corrosion using micro-computed tomography：literature review［J］. Construction and Building Materials，2021，284：122813.
[36]	WANG X F，CHEN Z P，REN J，et al. Object status identification of X-ray CT images of microcapsule-based self-healing mortar［J］. Cement & Concrete Composites，2022，125：104294.
[37]	ZENG Q，CHEN S，YANG P C，et al. Reassessment of mercury intrusion porosimetry for characterizing the pore structure of cement-based porous materials by monitoring the mercury entrapments with X-ray computed tomography［J］. Cement & Concrete Composites，2020，113：103726.
[38]	YANG Y G，ZHANG Y S，SHE W，et al. In situ observing the erosion process of cement pastes exposed to different sulfate solutions with X-ray computed tomography［J］. Construction and Building Materials，2018，176：556-565.
[39]	ITTY P A，SERDAR M，MERAL C，et al. In situ 3D monitoring of corrosion on carbon steel and ferritic stainless steel embedded in cement paste［J］. Corrosion Science，2014，83：409-418.
[40]	ZHANG X G，JIANG C，CHEN Y，et al. Study on the non-uniformity of rust layer and residual rebar caused by pitting corrosion in mortar［J］. Construction and Building Materials，2023，406：133442.
[41]	董征，付传清，陆晨涛，等. 基于钢筋加速非均匀锈蚀的混凝土保护层胀裂预测［J］. 西安建筑科技大学学报（自然科学版），2023，55（4）：598-606.
[42]	XU F，XIAO Y F，WANG S G，et al. Numerical model for corrosion rate of steel reinforcement in cracked reinforced concrete structure［J］. Construction and Building Materials，2018，180：55-67.
[43]	左桂琴. 基于保护层内部真实分布信息的滨海环境钢筋混凝土结构锈胀开裂3D原位研究［D］. 深圳：深圳大学，2019.
[44]	陈瑶. 基于钢筋混凝土内部非均匀锈层形貌的锈胀损伤研究［D］. 深圳：深圳大学，2022.