EFFECTS OF AGES ON FRACTURE PROPERTIES OF ORIENTED STEEL FIBER-REINFORCED CEMENTITIOUS COMPOSITES

QING Longbang; YANG Zhuofan; MU Ru

doi:10.13204/j.gyjzG20012801

Volume 51 Issue 1

Apr. 2021

Turn off MathJax

Article Contents

Article Navigation > INDUSTRIAL CONSTRUCTION > 2021 > 51(1): 146-151

QING Longbang, YANG Zhuofan, MU Ru. EFFECTS OF AGES ON FRACTURE PROPERTIES OF ORIENTED STEEL FIBER-REINFORCED CEMENTITIOUS COMPOSITES[J]. INDUSTRIAL CONSTRUCTION, 2021, 51(1): 146-151. doi: 10.13204/j.gyjzG20012801

Citation:

QING Longbang, YANG Zhuofan, MU Ru. EFFECTS OF AGES ON FRACTURE PROPERTIES OF ORIENTED STEEL FIBER-REINFORCED CEMENTITIOUS COMPOSITES[J]. INDUSTRIAL CONSTRUCTION, 2021, 51(1): 146-151. doi: 10.13204/j.gyjzG20012801

Citation:

PDF( 1153 KB)

EFFECTS OF AGES ON FRACTURE PROPERTIES OF ORIENTED STEEL FIBER-REINFORCED CEMENTITIOUS COMPOSITES

doi: 10.13204/j.gyjzG20012801

Department of Civil and Transportation Engineering, Hebei University of Technology, Tianjin 300401, China

Received Date: 2020-05-27
Available Online: 2021-04-30

Abstract

Abstract

The three-point bending tests on notched beams of different ages were conducted. The effects of ages on the fracture properties of oriented steel fiber-reinforced cementitious composites and randomly oriented steel fiber-reinforced cementitious composites were studied. Based on the curves of loadimg and crack opening displacement, the whole process of crack development of steel fiber-reinforced cementitious composites at different curing ages was analyzed. The results showed that, the flexural strength of steel fiber-reinforced cementitious composites increased with the increase of curing ages. The fracture energy of the composites increased rapidly in the stage of the first 7 days, and then slowed down and tended to be stable. When the volume contents of steel fiber varied from 1.2% to 2.0%, the fracture energy increased significantly, and the inprovement effect of the fracture energy of the composites was more obvious than that of randomly oriented fiber-reinforced cementitions conposites.
- age,
- oriented steel fiber,
- cementitious composite,
- flexural strength,
- fracture energy

FullText(HTML)

References(24)

References

ABRISHAMBAF A,PIMENTEL M,NUNES S.Influence of Fibre Orientation on the Tensile Behaviour of Ultra-High Performance Fibre Reinforced Cementitious Composites[J].Cement and Concrete Research,2017,97:28-40.

WIJFFELS M J H,WOLFS R J M,SUIKER A S J,et al.Magnetic Orientation of Steel Fibres in Self-Compacting Concrete Beams:Effect on Failure Behavior[J].Cement and Concrete Composites,2017,80:342-355.

KANG S T,KIM J K.Investigation on the Flexural Behavior of UHPCC Considering the Effect of Fiber Orientation Distribution[J].Construction and Building Materials,2012,28(1):57-65.

尤志国,付秀艳,周云龙,等.钢纤维混凝土抗弯性能及断面处纤维分布规律研究[J].工业建筑,2017,47(2):123-127.

高丹盈,张廷毅.三点弯曲下钢纤维高强混凝土的断裂性能[J].硅酸盐学报,2007,35(12):1630-1635.

杨松霖,刁波.钢纤维形状对超高性能纤维混凝土力学性能的影响[J].工业建筑,2012,42(1):140-143.

慕儒,王成,李辉,等.单向分布钢纤维增强水泥基复合材料(Ⅲ):断裂性能[J].建筑材料学报,2016,19(1):78-82.

张廷毅,李庆斌,汪自力,等.钢纤维高强混凝土断裂韧度及影响因素[J].硅酸盐学报,2012,40(5):638-645.

CARPINTERI A,BRIGHENTI R.Fracture Behaviour of Plain and Fiber-Reinforced Concrete with Different Water Content Under Mixed Mode Loading[J].Materials and Design,2010,31:2032-2042.

高淑玲,徐世烺,袁全,等.混杂钢纤维高强混凝土断裂特性研究[J].大连理工大学学报,2011(4):561-566.

CAGGIANO A,CREMONA M,FAELLA C,et al.Fracture Behavior of Concrete Beams Reinforced with Mixed Long/Short Steel Fibers[J].Construction and Building Materials,2012,37:832-840.

MICHELS J,CHRISTEN R,WALDMANN D.Experimental and Numerical Investigation on Postcracking Behavior of Steel Fiber Reinforced Concrete[J].Engineering Fracture Mechanics,2013,98:326-349.

王强,胡少伟,王阳.不同龄期混凝土断裂试验研究[J].人民长江,2018,49(9):91-97.

莫卓凯.龄期对全级配混凝土断裂特性的影响和混凝土K_R阻力曲线实用解析方法[D].大连:大连理工大学,2014.

NGUYEN D H,DAO V T N.A Novel Approach to Estimate the Evolution of Fracture Energy and Tensile Softening Curve of Concrete from Very Early Age[J].Engineering Fracture Mechanics,2018,196:43-55.

黄煜镔,钱觉时.龄期和养护方式对高强混凝土力学性能的影响[J].硅酸盐通报,2007,26(3):427-430.

HOOVER C G,ULM F J.Experimental Chemo-Mechanics of Early-Age Fracture Properties of Cement Paste[J].Cement and Concrete Research,2015,75:42-52.

金南国,金贤玉,郑砚国,等.早龄期混凝土断裂性能和微观结构的试验研究[J].浙江大学学报(工学版),2005,39(9):1374-1377.

MATALLAH M,FARAH M,GRONDIN F,et al.Size-Independent Fracture Energy of Concrete at Very Early Ages by Inverse Analysis[J].Engineering Fracture Mechanics,2013,109:1-16.

孙启林,王利民,韩昌瑞,等.早龄期钢纤维混凝土抗裂性能测试与计算[J].混凝土,2006(8):25-27.

BORDELON A,KIM M.Early-Age Fiber-Reinforced Concrete Properties for Overlays:MPC-492[R].Orem, Utah:Utah Vally University,2018.

FU C Q,MA Q Y,JIN X Y,et al.Fracture Property of Steel Fiber Reinforced Concrete at Early Age[J].Computers and Concrete,2014,13(1):31-47.

慕儒,李辉,王晓伟,等.单向分布钢纤维增强水泥基复合材料(Ⅱ):制备及钢纤维增强作用[J].建筑材料学报,2015,18(3):104-112.

RILEM T C.Draft Recommendation:Determination of the Fracture Energy of Mortar and Concrete by Means of Three-Point Bend Tests on Notched Beams[J].Materials and Structures,1985,18(6):484.

Relative Articles

Supplements(0)

Cited By

Proportional views