EXPERIMENTAL STUDY ON SALIFICATION EROSION RESISTANCE DURABILITY OF HIGH PERFORMANCE CONCRETE

Wang Mingfang; Sun Yuyong

doi:10.13204/j.gyjz201206027

Volume 42 Issue 6

Dec. 2014

Turn off MathJax

Article Contents

Abstract

References

Article Navigation > INDUSTRIAL CONSTRUCTION > 2012 > 42(6): 127-130

Wang Mingfang, Sun Yuyong. EXPERIMENTAL STUDY ON SALIFICATION EROSION RESISTANCE DURABILITY OF HIGH PERFORMANCE CONCRETE[J]. INDUSTRIAL CONSTRUCTION, 2012, 42(6): 127-130. doi: 10.13204/j.gyjz201206027

Citation:

Wang Mingfang, Sun Yuyong. EXPERIMENTAL STUDY ON SALIFICATION EROSION RESISTANCE DURABILITY OF HIGH PERFORMANCE CONCRETE[J]. INDUSTRIAL CONSTRUCTION, 2012, 42(6): 127-130. doi: 10.13204/j.gyjz201206027

Citation:

PDF( 0 KB)

EXPERIMENTAL STUDY ON SALIFICATION EROSION RESISTANCE DURABILITY OF HIGH PERFORMANCE CONCRETE

doi: 10.13204/j.gyjz201206027

1.
Department of Civil Engineering and Architecture,Tongling College,Tongling 244000,China

Received Date: 2011-07-25
Publish Date: 2012-06-20

Abstract

Abstract

Four groups of high performance concretes were designed, in which the content of pumice and zeolite wasdifferent, and twelve specimens were produced for each group. Three specimens had been eroded in lime saturatedwater, three in MgSO 4 solution, and three in NaCl solution for two years. Then the freezing and thawing experimenton them was done. In the experiment, the change of weight and compressive strength of high performance concretewhich had been eroded in different salification solutions was studied, meanwhile, the effects of different mineraladmixture on salification erosion resistance durability of high performance concrete were analyzed. The tests resultsshow that MgSO4solution' s erosion of high performance concrete is severer than NaCl solution, besides, salificationerosion resistance durability of high performance concrete with pumice and zeolite is good, and it increase with theincrease of zeolite content in high performance concrete.
- high performance concrete,
- salification erosion,
- durability,
- pumice,
- zeolite,
- freezing and thawing

FullText(HTML)

References(8)

References

赵霄龙，卫军，巴恒静.高性能混凝土在盐溶液中的抗冻性[J].建筑材料学报，2004，7(1):85-88.

[2] 张云清，余红发，王甲春.钢筋混凝土构件的抗盐冻性能研究[J].硅酸盐通报，2010，29(2):345-351.

[3] 王凤池，刘涛，刘磊，等.橡胶水泥土的抗盐蚀结晶性能[J].沈阳建筑大学学报:自然科学版，2009，25(4):630-634.

[4] 范宏，付燕弟，赵铁军.暴露21年后混凝土的碳化及氯离子侵入研究[J].工业建筑，2011，41(5):14-18，38.

[5] DemirI.The Usage Properties of Kaman Granites as Crushed Stone Aggregates[J].Gazi University Periodical of Institute of Science，2007，22(3):369-378.

[6] 赵年全.矿物掺合料对高性能混凝土力学和耐久性的影响分析[J].铁道建筑，2010(4):101-104.

[7] 谢友均，刘宝举，刘伟.矿物掺合料对高性能混凝土抗氯离子渗透性能的影响[J].铁道科学与工程学报，2004，1(2):46-51.

[8] 金祖权，赵铁军，孙伟.硫酸盐对混凝土腐蚀研究[J].工业建筑，2008，38(3):90-93.

Relative Articles

[1]	HAN Yudong, DING Xiaoping, HAO Tingyu, GUO Dong, HOU Dongwei. CURRENT STATUS OF RESEARCH ON DURABILITY OF SEAWATER-CORAL AGGREGATE CONCRETE[J]. INDUSTRIAL CONSTRUCTION, 2021, 51(2): 186-192,120. doi: 10.13204/j.gyjzG20042507
[2]	XUE Gang, ZHOU Haifeng, LIU Xiaowu, ZHANG Yue. EXPERIMENTAL STUDY ON BOND PROPERTIES BETWEEN RUBBER CONCRETE AND REBARS IN THE FREEZE-THAW ENVIRONMENT[J]. INDUSTRIAL CONSTRUCTION, 2021, 51(7): 107-112. doi: 10.13204/j.gyjzG19120306
[3]	NING Xiliang, WANG Wanping, HAO Shuai, ZHAO Zishun, ZHANG Fashan. EFFECT OF DIFFERENT FIBERS ON FROST RESISTANCE OF CONCRETE UNDER MULTIPLE FACTORS[J]. INDUSTRIAL CONSTRUCTION, 2020, 50(10): 122-128. doi: 10.13204/j.gyjzG19110401
[4]	Zhang Yiduo, Hu Qiangsheng, Chen Yu, Liu Ronggui. BENDING PERFORMANCE TEST AND NUMERICAL SIMULATION OF PRESTRESSED CONCRETE BEAMS AFTER FREEZE-THAW[J]. INDUSTRIAL CONSTRUCTION, 2015, 45(2): 27-31. doi: 10.13204/j.gyjz201502007
[5]	Li Yan, LüHenglin, Yin Huiguang, Zhang Lianying, Li Bing, Liu Ruixue. TEST RESEARCH ON THE FREEZING-THAWING RESISTANCE PERFORMANCE OF HIGH-STRENGTH CONCRETE WITH SINGLE ADMIXTURE AND DOUBLE ADMIXTURES[J]. INDUSTRIAL CONSTRUCTION, 2015, 45(2): 1-4. doi: 10.13204/j.gyjz201502001
[6]	Zhang Yiduo, Xu Lulu, Liu Ronggui, Liu Tao. STUDY ON DAMAGE OF PRE-STRESSED CONCRETE BEAMS IN THE ALTERNATIVE ACTION OF FREEZE-THAWING AND FATIGUE LOAD[J]. INDUSTRIAL CONSTRUCTION, 2013, 43(4): 57-61. doi: 10.13204/j.gyjz201304012
[7]	Wang Haiyan, Qiu Wenge, Man Shuai, Chen Xuefeng. EXPERIMENTAL RESEARCH ON HIGH-PERFORMANCE CONCRETE TUNNEL LINING BASED ON COMPOSITE CEMENTITIOUS MATERIAL[J]. INDUSTRIAL CONSTRUCTION, 2013, 43(9): 111-115. doi: 10.13204/j.gyjz201309021
[8]	Wang Chenfei, Niu Ditao. RESEARCH ON THE DURABILITY OF POLYPROPYLENE FIBER CONCRETE UNDER FREEZE-THAW DAMAGE[J]. INDUSTRIAL CONSTRUCTION, 2012, 42(1): 137-139,153. doi: 10.13204/j.gyjz201201026
[9]	Sui Lili, Quan Xinrui, Xing Feng, Zhang Hongyuan. STATE-OF-THE-ART OF RESEARCH ON DURABILITY OF POST-TENSIONED CONCRETE BRIDGES[J]. INDUSTRIAL CONSTRUCTION, 2011, 41(1): 105-111. doi: 10.13204/j.gyjz201101025
[10]	Li Fuhai, Zhao Renda, Ye Yuezhong. STUDY ON EROSION-RESISTING CHARACTERISTICS OF CONCRETE UNDER FREEZING-THAWING ACTION[J]. INDUSTRIAL CONSTRUCTION, 2010, 40(6): 1-4. doi: 10.13204/j.gyjz201006001
[11]	Wang Lei, Zhao Yanlin. RESEARCH ON THE DURABILITY OF CORRODED RC BEAMS STRENGTHENED WITH CARBON FIBERS IN MARINE CONDITIONS[J]. INDUSTRIAL CONSTRUCTION, 2009, 39(8): 120-124. doi: 10.13204/j.gyjz200908029
[12]	Huo Junfang, Shen Xiangdong. THE EXPERIMENT STUDY ON FROST RESISTANCE DURABILITY OF POLYPROPYLENE FIBER REINFORCED LIGHTWEIGHT AGGREGATE CONCRETE[J]. INDUSTRIAL CONSTRUCTION, 2009, 39(3): 86-89. doi: 10.13204/j.gyjz200903024
[13]	Li Shengyong, Zhang Zhe, Gong Jinxin. A NEW DURABILITY DESIGN METHOD FOR CONCRETE STRUCTURES BASED ON EQUIVALENT RESISTANCE RELIABILITY[J]. INDUSTRIAL CONSTRUCTION, 2007, 37(8): 77-81. doi: 10.13204/j.gyjz200708020
[14]	Gao Dan-ying, Xie Xiao-peng. PERFORMANCE OF STEEL FIBER REINFORCED CONCRETE UNDER THE ACTION OF FREEZE-THAW CIRCULATION[J]. INDUSTRIAL CONSTRUCTION, 2006, 36(10): 65-68. doi: 10.13204/j.gyjz200610018
[15]	Song Shao-min, Geng Lei. THE STUDY ON IMPERMEABILITY AND FREEZING RESISTANCE OF HIGH PERFORMANCE CONCRETE WITH ARTIFICIAL SAND[J]. INDUSTRIAL CONSTRUCTION, 2006, 36(7): 68-70,99. doi: 10.13204/j.gyjz200607018
[16]	Sun Daosheng, Deng Min, Tang Mingshu. STUDY ON THE DURABILITY OF THE FIBER AND HYBRID FIBER REINFORCED EXPANSIVE CONCRETE[J]. INDUSTRIAL CONSTRUCTION, 2005, 35(4): 69-71,47. doi: 10.13204/j.gyjz200504020
[17]	Zhang Leishun, Wang Juan, Huang Qiufeng, Deng Yu. EXPERIMENTAL STUDY ON FROST-RESISTANT DURABILITY OF RECYCLED CONCRETE[J]. INDUSTRIAL CONSTRUCTION, 2005, 35(9): 64-66,45. doi: 10.13204/j.gyjz200509017
[18]	Zhou Xingang, Chu Mingjin, Wu Jianglong, Li Qiang, Sui Zhijun, Gao Zhongqin. DURABILITY OF CONCRETE STRUCTURES EXPOSED TO UNFAVORABLE ATMOSPHERE[J]. INDUSTRIAL CONSTRUCTION, 2004, 34(4): 66-68,65. doi: 10.13204/j.gyjz200404019
[19]	Xiao Jianzhuang, Lu Fuhai, Sun Zhenping. STUDY ON CHLORIDE ION PERMEABILITY OF HIGH PERFORMANCE CONCRETE WITH DESALTED SEA SAND[J]. INDUSTRIAL CONSTRUCTION, 2004, 34(5): 4-6,14. doi: 10.13204/j.gyjz200405002