RESEARCH ON THE DURABILITY OF POLYPROPYLENE FIBER CONCRETE UNDER FREEZE-THAW DAMAGE

Wang Chenfei; Niu Ditao

doi:10.13204/j.gyjz201201026

Volume 42 Issue 1

Dec. 2014

Turn off MathJax

Article Contents

Abstract

References

Article Navigation > INDUSTRIAL CONSTRUCTION > 2012 > 42(1): 137-139,153

Wang Chenfei, Niu Ditao. RESEARCH ON THE DURABILITY OF POLYPROPYLENE FIBER CONCRETE UNDER FREEZE-THAW DAMAGE[J]. INDUSTRIAL CONSTRUCTION, 2012, 42(1): 137-139,153. doi: 10.13204/j.gyjz201201026

Citation:

Wang Chenfei, Niu Ditao. RESEARCH ON THE DURABILITY OF POLYPROPYLENE FIBER CONCRETE UNDER FREEZE-THAW DAMAGE[J]. INDUSTRIAL CONSTRUCTION, 2012, 42(1): 137-139,153. doi: 10.13204/j.gyjz201201026

Wang Chenfei, Niu Ditao. RESEARCH ON THE DURABILITY OF POLYPROPYLENE FIBER CONCRETE UNDER FREEZE-THAW DAMAGE[J]. INDUSTRIAL CONSTRUCTION, 2012, 42(1): 137-139,153. doi: 10.13204/j.gyjz201201026

Citation:

Wang Chenfei, Niu Ditao. RESEARCH ON THE DURABILITY OF POLYPROPYLENE FIBER CONCRETE UNDER FREEZE-THAW DAMAGE[J]. INDUSTRIAL CONSTRUCTION, 2012, 42(1): 137-139,153. doi: 10.13204/j.gyjz201201026

PDF( 0 KB)

RESEARCH ON THE DURABILITY OF POLYPROPYLENE FIBER CONCRETE UNDER FREEZE-THAW DAMAGE

doi: 10.13204/j.gyjz201201026

1.
School of Civil Engineering,Xi'an University of Architecture and Technology,Xi'an 710055,China

Received Date: 2011-05-17
Publish Date: 2012-01-20

Abstract

Abstract

In order to study the Cl-migration under freeze-thaw cycle and the freeze-deicing salt scaling resistance of polypropylene fiber concrete with different volume,indoor artificial method was used to simulate freeze-thaw cycle.The results indicated that the scaled mass and relative dynamic modulus of elasticity loss decrease with the volume of fiber increasing,Cl-concentration had a enrichment near the sample surface,adding 0.1% PPF into concrete had the prefect resistance of deicer-frost scaling.More fibers could delay the development of cracks,but that would reduce the inner density of concrete.
- polypropylene fiber,
- concrete,
- durability,
- deicer-frost damage,
- chloride ion

FullText(HTML)

References(11)

References

杨全兵. 混凝土盐冻破坏机理(I)--毛细管饱水度和结冰压[J].建筑材料学报,2007,(05):523-527.

Pigeon M,Marchand J,Pleau R. Frost Resistant Concrete[J].Construction and Building Materials,1996,(05):339-348.

Mieahal A G,Marek Z. Frost Salt Scaling Resistance of Concrete Containing CFBC Fly Ash[J].Materials and Structures,2008,(05):33-42.

Micah H W. Examining the Frost Resistance of High Performance Concrete[J].Construction and Building Materials,2009,(23):878-888.

贡金鑫,何世钦,郭育霞. 盐环境中冻融循环对钢筋与混凝土黏结性能影响[J].大连理工大学学报,2005,(03):405-409.

陈少峰,孙立,李振宝. 混凝土盐冻破坏的试验研究[J].公路,2006,(04):216-219.

张礼和,谈慕华,马一平. PP纤维水泥截面粘结与抗干缩开裂性能研究[J].建筑材料学报,2001,(01):18-21.

盛松涛,方坤河. 聚丙烯纤维在水工高性能混凝士中的作用[J].混凝土,2003,(11):51-54.

黄士元,杨全兵. 高抗冻融高抗盐剥蚀混凝土路面的研究与应用[J].黑龙江交通科技,2000,(增刊):45-55.

JTJ270-98水运工程混凝土试验规程[S].The Journal of Biochemistry,2009,(2).

何富强,史才军,元强. 硝酸银显色法变色边界处氯离子浓度的影响因素[J].硅酸盐学报,2008,(07):890-895.

Relative Articles

[1]	ZHONG Xiaoping, XU Jiahao, LIU Yang, XIA Jin, ZHU Bingxi, ZHANG Jun, NI Keting. Effects of Loads and Erosion Dimensions on the Chloridion Transmission Rule in Concrete[J]. INDUSTRIAL CONSTRUCTION, 2024, 54(10): 205-214. doi: 10.3724/j.gyjzG24022706
[2]	ZHAO Peng, ZHANG Xizhe, SHEN Jian, CHEN Jiejing, YU Ben, JIN Weiliang, XIA Jin. Influence of Spatial Distribution of Chloride Ion Concentration on Non-Uniform Corrosion of Reinforcement in Concrete[J]. INDUSTRIAL CONSTRUCTION, 2023, 53(3): 201-207. doi: 10.13204/j.gyjzG22070305
[3]	SHEN Caihua, CHEN Wei, CHEN Xiaofeng, XIE Fei, LYU Shiming, XU Xiuliang. Chloride Diffusion Model and Diffusion Law Analysis of Concrete Based on GEM Equation[J]. INDUSTRIAL CONSTRUCTION, 2022, 52(7): 151-158. doi: 10.13204/j.gyjzG20122608
[4]	HAN Yudong, DING Xiaoping, HAO Tingyu, GUO Dong, HOU Dongwei. CURRENT STATUS OF RESEARCH ON DURABILITY OF SEAWATER-CORAL AGGREGATE CONCRETE[J]. INDUSTRIAL CONSTRUCTION, 2021, 51(2): 186-192,120. doi: 10.13204/j.gyjzG20042507
[5]	NING Xiliang, WANG Wanping, HAO Shuai, ZHAO Zishun, ZHANG Fashan. EFFECT OF DIFFERENT FIBERS ON FROST RESISTANCE OF CONCRETE UNDER MULTIPLE FACTORS[J]. INDUSTRIAL CONSTRUCTION, 2020, 50(10): 122-128. doi: 10.13204/j.gyjzG19110401
[6]	Su Xiaoping, Zhang Li, Guo Jinhui. EXPERIMENTAL STUDY OF CONCRETE DURABILITY UNDER THE ACTION OF SINGLE SALT CORROSION AND FREEZING-THAWING CYCLES[J]. INDUSTRIAL CONSTRUCTION, 2014, 44(09): 110-113.
[7]	Wang Zhendi, Yao Yan, Wang Ling, Cao Yin. PERMEABILITY OF STEEL SLAG AND BLAST FURNACE SLAGE CONCRETE EXPOSED TO SALT FROST[J]. INDUSTRIAL CONSTRUCTION, 2013, 43(2): 113-116,158. doi: 10.13204/j.gyjz201302023
[8]	Yan Yongdong, Lu Chunhua, Liu Ronggui. EXPERIMENTS OF CHLORIDE INGRESSION IN COMPRESIVE STRESSED CONCRETE[J]. INDUSTRIAL CONSTRUCTION, 2013, 43(1): 75-79. doi: 10.13204/j.gyjz201301017
[9]	Zhao Huimin, Wang Jun, Liu Weiqing, Fang Hai, Zhou Hongwei. EXPERIMENTAL STUDY OF DURABILITY OF GFRP UNDER COUPLING EFFECT OF CHLORIDE ION WITH LOADING[J]. INDUSTRIAL CONSTRUCTION, 2013, 43(10): 102-105. doi: 10.13204/j.gyjz201310022
[10]	Wang Jianmin, Liu Guanguo, Lei Xiao, Li Di, Ma Hu. EXPERIMENTAL STUDY ON THE ANTI-CHLORIDE ION PERFORMANCE OF CONCRETE IN SALT SPRAY ENVIRONMENT[J]. INDUSTRIAL CONSTRUCTION, 2013, 43(11): 89-91,125. doi: 10.13204/j.gyjz201311020
[11]	Yan Yongdong, Jin Weiliang, Wang Hailong. INFLUENCE OF SELF-HEALING ON CHLORIDE ION INGRESS IN CRACKED CONCRETE[J]. INDUSTRIAL CONSTRUCTION, 2011, 41(5): 6-9. doi: 10.13204/j.gyjz201105002
[12]	Zhang Junzhi, Wang Jianze, Zhou Jianmin, Zheng Hui. STUDY ON CHLORIDE IONS EROSION AND RANDOMNESS FOR EXISTING CONCRETE IN NATURAL ENVIRONMENT[J]. INDUSTRIAL CONSTRUCTION, 2009, 39(3): 77-80. doi: 10.13204/j.gyjz200903022
[13]	Wang Lei, Zhao Yanlin. RESEARCH ON THE DURABILITY OF CORRODED RC BEAMS STRENGTHENED WITH CARBON FIBERS IN MARINE CONDITIONS[J]. INDUSTRIAL CONSTRUCTION, 2009, 39(8): 120-124. doi: 10.13204/j.gyjz200908029
[14]	Huo Junfang, Shen Xiangdong. THE EXPERIMENT STUDY ON FROST RESISTANCE DURABILITY OF POLYPROPYLENE FIBER REINFORCED LIGHTWEIGHT AGGREGATE CONCRETE[J]. INDUSTRIAL CONSTRUCTION, 2009, 39(3): 86-89. doi: 10.13204/j.gyjz200903024
[15]	Ma Kunlin, Xie Youjun, Long Guangcheng, Shi Mingxia. STUDY ON PREPARATION OF HIGH PERFORMANCE CONCRETE WITH IMPERMEABILITY TO CHLORIDE IONS[J]. INDUSTRIAL CONSTRUCTION, 2006, 36(11): 90-93. doi: 10.13204/j.gyjz200611022
[16]	Hu Yanjun, . THE TIME-DEPENDENT CHLORIDE PERMEABILITY OF BLENDED CONCRETE[J]. INDUSTRIAL CONSTRUCTION, 2006, 36(12): 9-11,8. doi: 10.13204/j.gyjz200612003
[17]	Huang Pengfei, Bao Yiwang, Yao Yan. DAMAGES OF REINFORCED CONCRETE UNDER SYNERGISTIC EFFECTS OF CYCLIC FREEZE-THAW, DEICING-SALT ATTACK, REBAR CORROSION AND BENDING LOAD[J]. INDUSTRIAL CONSTRUCTION, 2005, 35(5): 63-67. doi: 10.13204/j.gyjz200505017
[18]	Zhang Leishun, Wang Juan, Huang Qiufeng, Deng Yu. EXPERIMENTAL STUDY ON FROST-RESISTANT DURABILITY OF RECYCLED CONCRETE[J]. INDUSTRIAL CONSTRUCTION, 2005, 35(9): 64-66,45. doi: 10.13204/j.gyjz200509017
[19]	Tu Yongming, LüZhitao. THE EXPERIMENTAL RESEARCH ON PRESTRESSED CONCRETE STRUCTURE UNDER SALT FOG CORROSION ENVIRONMENT[J]. INDUSTRIAL CONSTRUCTION, 2004, 34(5): 1-3,10. doi: 10.13204/j.gyjz200405001
[20]	Zhou Xingang, Chu Mingjin, Wu Jianglong, Li Qiang, Sui Zhijun, Gao Zhongqin. DURABILITY OF CONCRETE STRUCTURES EXPOSED TO UNFAVORABLE ATMOSPHERE[J]. INDUSTRIAL CONSTRUCTION, 2004, 34(4): 66-68,65. doi: 10.13204/j.gyjz200404019