EXPERIMENTAL RESEARCH ON CHLORIDE THRESHOLD LEVEL OF STEEL CORROSION IN SYNTHETIC PORE SOLUTION UNDER HIGH TEMPERATURE

Zhou Jianting; Song Xiaobing

doi:10.13204/j.gyjz201105003

Volume 41 Issue 5

Dec. 2014

Turn off MathJax

Article Contents

Article Navigation > INDUSTRIAL CONSTRUCTION > 2011 > 41(5): 10-13,22

Zhou Jianting, Song Xiaobing. EXPERIMENTAL RESEARCH ON CHLORIDE THRESHOLD LEVEL OF STEEL CORROSION IN SYNTHETIC PORE SOLUTION UNDER HIGH TEMPERATURE[J]. INDUSTRIAL CONSTRUCTION, 2011, 41(5): 10-13,22. doi: 10.13204/j.gyjz201105003

Citation:

Zhou Jianting, Song Xiaobing. EXPERIMENTAL RESEARCH ON CHLORIDE THRESHOLD LEVEL OF STEEL CORROSION IN SYNTHETIC PORE SOLUTION UNDER HIGH TEMPERATURE[J]. INDUSTRIAL CONSTRUCTION, 2011, 41(5): 10-13,22. doi: 10.13204/j.gyjz201105003

Citation:

PDF( 0 KB)

EXPERIMENTAL RESEARCH ON CHLORIDE THRESHOLD LEVEL OF STEEL CORROSION IN SYNTHETIC PORE SOLUTION UNDER HIGH TEMPERATURE

doi: 10.13204/j.gyjz201105003

1.
Department of Civil Engineering,Shanghai Jiaotong University,Shanghai 200240,China

Received Date: 2009-11-23
Publish Date: 2011-05-20

Abstract

Abstract

The steel rebar inside reinforced concrete structures is susceptible to corrosion when Cl-content at the surface of the steel exceeding a chloride threshold level(CTL).The CTL is an important influence on the service life of concrete structures exposed to chloride environments.Especially in high temperature regions, reinforced concrete structures are more severely damaged.The paper focused on studying the influence of high temperature on CTL.The experiment was carried out in 50 ℃ synthetic pore solution, considering the influences of electric potentials and pHs, and CTL of 95% acceptance value achieved.Results show that CTL under 50 ℃ is much smaller than that under normal temperature(25 ℃), and the controlling effect of temperature is more obvious as the corrosion potential decreases and pH value increases.Fitting curve of CTL to temperature was also presented.
- high temperature,
- steel corrosion,
- chloride threshold level( CTL),
- influence of temperature

FullText(HTML)

References(14)

References

[1] Arup H. The Mechanics of the Protection of Steel by Concrete?[C]∥ Society of Chemical Industrial Conference of Reinforcement?in Concrete Construction,1983.

[2] 张誉.混凝土结构耐久性概论[M].上海:上海科学技术出版社,2003.

[3] FIB. Model Code for Service Life Design [M]. Bulletin:?Federation International du Beton,2006.

[4] Manera M, Vennesland O, Bertolini L. Chloride Threshold for?Rebar Corrosion in Concrete with Addition of Silica Fume [J]. Corrosion Science,2008(50):544-560.

[5] Glass G K, Buenfeld N R. Chloride Threshold Level for Corrosion?of Steel in Concrete [J]. Corrosion Science,1997(39):1001-1013.

[6] Alonso C , Andrade C , Castellote M, et al. Chloride Threshold?Values to Depassivate Reinforcing Bars Embedded in a?Standardized OPC Mortar [J]. Cement and Concrete Research,2000(30):1047-1055.

[7] Broomfield J P. Corrosion of Steel in Concrete: Understanding,?Investigation and Repair [M]. London: E FN Spon,1997.

[8] 陈卿.钢筋腐蚀临界氯离子浓度的试验研究[D].上海:上海交通大学,2008.

[9] Poursaee A, Hansson C M. Reinforcing Steel Passivation in Mortar?and Pore Solution [J]. Cement Concrete Research,2007,37(7):1127-1133.

[10] 陈卿,宋晓冰,翟之阳.混凝土模拟孔隙液中钢筋腐蚀临界氯离子浓度试验研究[J].四川建筑科学研究,2008,34(6):156-162.

[11] Izquierdo D. Potentiostatic Determination of Chloride Threshold?Values for Rebar Depassivation: Experimental and Statistical?Study [J]. Electrochimica Acta,2004,49(17/18):2731-2739.

[12] Hussain S E, Rasheeduzzafar, Al-Musallam A. Factors Affecting?Threshold Chloride for Reinforcement Corrosion in Concrete [J]. Cement and Concrete Research,1995;25(7):1543-1555.

[13] 洪定海.混凝土中钢筋的腐蚀与保护[M].北京:中国铁道出版社,1998.

Relative Articles

Supplements(0)

Cited By

Proportional views