Experimental Study on Mechanical Properties of Basalt-Fiber-Reinforced Nano-SiO<sub>2</sub> Concrete After Being Subjected to High Temperatures

LIU Huaxin; ZHENG Taiyuan

doi:10.13204/j.gyjzG20092909

Volume 52 Issue 2

Feb. 2022

Turn off MathJax

Article Contents

Article Navigation > INDUSTRIAL CONSTRUCTION > 2022 > 52(2): 18-23,107

LIU Huaxin, ZHENG Taiyuan. Experimental Study on Mechanical Properties of Basalt-Fiber-Reinforced Nano-SiO2 Concrete After Being Subjected to High Temperatures[J]. INDUSTRIAL CONSTRUCTION, 2022, 52(2): 18-23,107. doi: 10.13204/j.gyjzG20092909

Citation:

LIU Huaxin, ZHENG Taiyuan. Experimental Study on Mechanical Properties of Basalt-Fiber-Reinforced Nano-SiO₂ Concrete After Being Subjected to High Temperatures[J]. INDUSTRIAL CONSTRUCTION, 2022, 52(2): 18-23,107. doi: 10.13204/j.gyjzG20092909

Citation:

PDF( 3189 KB)

Experimental Study on Mechanical Properties of Basalt-Fiber-Reinforced Nano-SiO₂ Concrete After Being Subjected to High Temperatures

doi: 10.13204/j.gyjzG20092909

LIU Huaxin^1,2,
ZHENG Taiyuan²

1. Southeast University, Key Laboratory of Concrete and Pre-Stressed Concrete Structures of Ministry of Education, Nanjing 210018, China;
2. School of Civil Engineering and Architecture, Liaoning University of Technology, Jinzhou 121001, China

Received Date: 2020-09-29
Available Online: 2022-06-30
Publish Date: 2022-02-20

Abstract

Abstract

The compressive, splitting tensile and flexural tests of plain concrete, nano-SiO₂ concrete and basalt fiber nano-SiO₂ concrete under high temperatures were carried out, and the prediction model of concrete strength that was established. According to the results, the compressive strength of each group reached a peak value at 400 ℃, at that time, each group of concrete at normal temperature increased by about 3.5% to 6.8%, and then decreased gradually, and the splitting tensile strength and flexural strength decreased gradually with the increase of temperature, at 800 ℃, the residual ratios of cracking and pulling strength and the residual ratios of flexural strength were 27.6% and 36.2%, respectively. Adding nano-SiO₂ could improved the compressive, splitting tensile and flexural strength of plain concrete. The compressive strength, splitting tensile strength and flexural strength of nano-SiO₂ concrete after being subjected to 800 ℃ high temperature were increased by 33.7%,15.6% and 17.2% respectively. The accuracy of concrete strength prediction after being subjected to high temperatures was high.
- basalt fiber,
- nano-SiO₂ concrete,
- high temperature,
- mechanical property

FullText(HTML)

References(15)

References

[1]	赵燕茹,刘道宽,王磊,等.玄武岩纤维混凝土高温后力学性能试验研究[J].混凝土,2019(10):72-75.
[2]	朴战东.高温后玄武岩纤维混凝土力学性能试验研究[D].郑州:郑州大学,2016.
[3]	秦毓雯.玄武岩纤维混凝土高温后耐久性能研究[D].徐州:中国矿业大学,2020.
[4]	戎虎仁,王海龙,褚少辉,等.高温作用下不同掺量玄武岩纤维混凝土力学性能研究[J].粉煤灰综合利用,2020,34(1):56-60.
[5]	SIM J, PARK C, MOON D Y. Characteristics of basalt fiber as a strengthening material for concrete structures[J]. Composites:Part B, 2005, 36(6):504-512.
[6]	HIGH C, SELIEM H M, EL-SAFTY A, et al. Use of basalt fibers for concrete structures[J]. Construction and Building Materials, 2015, 96:37-46.
[7]	邱国洲,房建宏,徐安花,等.玄武岩纤维沥青混凝土高温性能研究[J].硅酸盐通报,2019,38(12):3890-3896.
[8]	徐光洁.掺纳米材料混凝土耐久性研究综述[J].四川建材,2011,37(5):272-274.
[9]	KAWASHIMA S, HOU P, CORR D J, et al. Modification of cement-based materials with nanoparticles[J]. Cement&Concrete Composites, 2016, 36(1):8-15.
[10]	SHIH J, HSIAO T. Effect of nanosilica on characterization of Portland cement composite[J]. Materials Science and Engineering:A, 2006, 424(1/2):266-274.
[11]	陈刚,高丹盈,王东,等.钢纤维纳米SiO₂混凝土强度的试验研究[J].河北工业大学学报,2014,43(6):77-80.
[12]	GUNEYISI E, GESOGLU M, AZEZ O A, et al. Effect of nano silica on the workability of self-compacting concretes having untreated and surface treated lightweight aggregates[J]. Construction and Building Materials, 2016.DOI:10.1.16.cong uildmat.2016.04.055.
[13]	CHITHRA S, KUMAR S, CHINNARAJU K, et al. A comparative study on the compressive strength prediction models for high performance concrete containing nano silica and copper slag using regression analysis and Artificial Neural Networks[J]. Construction and Building Materials, 2016(114):528-535.
[14]	燕兰,邢永明.纳米SiO₂对钢纤维/混凝土高温后力学性能及微观结构的影响[J].复合材料学报,2013,30(3):133-141.
[15]	李曈,张晓东,刘华新,等.高温后混杂纤维混凝土力学性能试验研究[J].铁道科学与工程学报,2020,17(5):1171-1177.