STUDY OF THE TENSILE PROPERTIES OF DOMESTIC CARBON FIBERS

Wang Zike; Xian Guijun; Li Hui

doi:10.13204/j.gyjz201306001

Volume 43 Issue 6

Dec. 2014

Turn off MathJax

Article Contents

Article Navigation > INDUSTRIAL CONSTRUCTION > 2013 > 43(6): 1-4

Wang Zike, Xian Guijun, Li Hui. STUDY OF THE TENSILE PROPERTIES OF DOMESTIC CARBON FIBERS[J]. INDUSTRIAL CONSTRUCTION, 2013, 43(6): 1-4. doi: 10.13204/j.gyjz201306001

Citation:

Wang Zike, Xian Guijun, Li Hui. STUDY OF THE TENSILE PROPERTIES OF DOMESTIC CARBON FIBERS[J]. INDUSTRIAL CONSTRUCTION, 2013, 43(6): 1-4. doi: 10.13204/j.gyjz201306001

Wang Zike, Xian Guijun, Li Hui. STUDY OF THE TENSILE PROPERTIES OF DOMESTIC CARBON FIBERS[J]. INDUSTRIAL CONSTRUCTION, 2013, 43(6): 1-4. doi: 10.13204/j.gyjz201306001

Citation:

Wang Zike, Xian Guijun, Li Hui. STUDY OF THE TENSILE PROPERTIES OF DOMESTIC CARBON FIBERS[J]. INDUSTRIAL CONSTRUCTION, 2013, 43(6): 1-4. doi: 10.13204/j.gyjz201306001

PDF( 0 KB)

STUDY OF THE TENSILE PROPERTIES OF DOMESTIC CARBON FIBERS

doi: 10.13204/j.gyjz201306001

1.
School of Civil Engineering,Harbin Institute of Technology,Harbin 150090,China

Received Date: 2013-01-25
Publish Date: 2013-06-20

Abstract

Abstract

The tensile mechanical properties of single carbon fibers produced in China were tested.The Weibull distribution function was used to analyze the testing results.It is found that the tensile strength of the domestic carbon fibers is much lower than that of Toray T700 and TC36S carbon fibers.Scanning electron microscope(SEM) analysis shows that the surface of Toray T700 carbon fiber is smooth, and there are shallow grooves on the surface of TC36S carbon fiber;whereas there are wider and deeper groover on the surface of domestic carbon fiber.Which may be responsible for relatively lower tensile strengths.
- domestic carbon fibers,
- filament tensile test,
- mechanical properties,
- surface structures

FullText(HTML)

References(12)

References

叶列平,冯鹏.FRP 在工程结构中的应用与发展[J].土木工程学报,2006,39(3):24－36.

[2] 冯丽,闻艳萍．我国碳纤维的发展现状及建议[J].进展与评述,2012(1):5－8.

[3] 李勇,肖军,张唐领.M46 J 高模量碳纤维预浸 QY8911纤维束性能研究[J].南京航空航天大学学报,2002,34(3):266－269.

[4] 张为芹,田艳红．高强碳纤维束丝拉伸性能测试影响因素的研究[J].理化检验－物理分册,2006,42(11):541－543.

[5] 吴琪琳,潘鼎．碳纤维强度的 WEIBULL 分析理论[J].高科技纤维与应用,1999,24(6):41－44.

[6] 李雪梅,王继辉,高国强,等．单纤维复合材料断裂实验表征界面研究[J].武汉理工大学学报,2005,27(4):9－12.

[7] 邓传斌,钱振明,段文江．纤维树脂界面剪切强度及纤维强度分布参数的实验测定[J].实验力学,1997,12(2):204－208.

[8] Koyanagi J,Hatta H,Kotani M,et al.A Comprehensive Model?for Determining Tensile Strengths of Various Unidirectional?Composites[J].Journal of Composite Materials,2009,43(18):1901－1914.

[9] Weibull W,Stockholm,Sweden.A Statistical Distribution?Function of Wide Applicability [J].Journal of Applied?Mechanics,1951,18:293－297.

[10] 吴琪琳．不同拉伸条件下基于 Weibull 模型的粘胶基碳纤维强度分布研究[J].合成纤维工业,2002,25(2):25－28.

[11] 武玉芬,张博明．碳纤维拉伸强度的离散性分析[J].玻璃钢/复合材料,2010(3):29－30.

[12] 侯锋辉,邓红兵,李崇俊,等．碳纤维结构的常用表征技术[J].纤维复合材料,2008(3):18－20．

Relative Articles

Supplements(0)

Cited By

Proportional views