EXPERIMENTAL STUDY ON SALIFICATION EROSION RESISTANCE DURABILITY OF HIGH PERFORMANCE CONCRETE

Wang Mingfang; Sun Yuyong

doi:10.13204/j.gyjz201206027

Volume 42 Issue 6

Dec. 2014

Turn off MathJax

Article Contents

Article Navigation > INDUSTRIAL CONSTRUCTION > 2012 > 42(6): 127-130

Wang Mingfang, Sun Yuyong. EXPERIMENTAL STUDY ON SALIFICATION EROSION RESISTANCE DURABILITY OF HIGH PERFORMANCE CONCRETE[J]. INDUSTRIAL CONSTRUCTION, 2012, 42(6): 127-130. doi: 10.13204/j.gyjz201206027

Citation:

Wang Mingfang, Sun Yuyong. EXPERIMENTAL STUDY ON SALIFICATION EROSION RESISTANCE DURABILITY OF HIGH PERFORMANCE CONCRETE[J]. INDUSTRIAL CONSTRUCTION, 2012, 42(6): 127-130. doi: 10.13204/j.gyjz201206027

Citation:

PDF( 0 KB)

EXPERIMENTAL STUDY ON SALIFICATION EROSION RESISTANCE DURABILITY OF HIGH PERFORMANCE CONCRETE

doi: 10.13204/j.gyjz201206027

1.
Department of Civil Engineering and Architecture,Tongling College,Tongling 244000,China

Received Date: 2011-07-25
Publish Date: 2012-06-20

Abstract

Abstract

Four groups of high performance concretes were designed, in which the content of pumice and zeolite wasdifferent, and twelve specimens were produced for each group. Three specimens had been eroded in lime saturatedwater, three in MgSO 4 solution, and three in NaCl solution for two years. Then the freezing and thawing experimenton them was done. In the experiment, the change of weight and compressive strength of high performance concretewhich had been eroded in different salification solutions was studied, meanwhile, the effects of different mineraladmixture on salification erosion resistance durability of high performance concrete were analyzed. The tests resultsshow that MgSO4solution' s erosion of high performance concrete is severer than NaCl solution, besides, salificationerosion resistance durability of high performance concrete with pumice and zeolite is good, and it increase with theincrease of zeolite content in high performance concrete.
- high performance concrete,
- salification erosion,
- durability,
- pumice,
- zeolite,
- freezing and thawing

FullText(HTML)

References(8)

References

赵霄龙，卫军，巴恒静.高性能混凝土在盐溶液中的抗冻性[J].建筑材料学报，2004，7(1):85-88.

[2] 张云清，余红发，王甲春.钢筋混凝土构件的抗盐冻性能研究[J].硅酸盐通报，2010，29(2):345-351.

[3] 王凤池，刘涛，刘磊，等.橡胶水泥土的抗盐蚀结晶性能[J].沈阳建筑大学学报:自然科学版，2009，25(4):630-634.

[4] 范宏，付燕弟，赵铁军.暴露21年后混凝土的碳化及氯离子侵入研究[J].工业建筑，2011，41(5):14-18，38.

[5] DemirI.The Usage Properties of Kaman Granites as Crushed Stone Aggregates[J].Gazi University Periodical of Institute of Science，2007，22(3):369-378.

[6] 赵年全.矿物掺合料对高性能混凝土力学和耐久性的影响分析[J].铁道建筑，2010(4):101-104.

[7] 谢友均，刘宝举，刘伟.矿物掺合料对高性能混凝土抗氯离子渗透性能的影响[J].铁道科学与工程学报，2004，1(2):46-51.

[8] 金祖权，赵铁军，孙伟.硫酸盐对混凝土腐蚀研究[J].工业建筑，2008，38(3):90-93.

Relative Articles

Supplements(0)

Cited By

Proportional views