460 MPa耐火钢高温泊松比试验研究

王连庆; 王红缨; 马文江

doi:10.13204/j.gyjzG20072607

460 MPa耐火钢高温泊松比试验研究

doi: 10.13204/j.gyjzG20072607

1. 北京科技大学新金属材料国家重点实验室, 北京 100083;
2. 北京科技大学数理学院, 北京 100083

基金项目:

国家重点研发计划项目（2017YFB0304700）。

详细信息

作者简介:
王连庆,男,1967年出生,博士,高级工程师。电子信箱:lqwang@skl.ustb.edu.cn

计量
- 文章访问数: 77
- HTML全文浏览量: 7
- PDF下载量: 1
- 被引次数: 0
出版历程
- 收稿日期: 2020-10-20
- 网络出版日期: 2021-07-17

EXPERIMENTAL RESEARCH ON POISSON'S RATIOS OF 460 MEGAPASCAL HEAT-RESISTING STEEL AT HIGH TEMPERATURE

1. State Key Laboratory for Advanced Metals & Materials, University of Science and Technology Beijing, Beijing 100083, China;
2. School of Mathematics and Physics, University of Science and Technology Beijing, Beijing 100083, China

摘要

摘要: 为测量460 MPa耐火钢的高温泊松比，在MTS809材料试验机上，完成460 MPa耐火钢室温、高温100~600℃拉伸与扭转试验，利用高温拉扭引伸计测定材料在不同温度下的弹性模量与剪切模量，根据泊松比、弹性模量与剪切模量的关系式，计算得到材料的高温泊松比。利用室温径向与轴向引伸计，通过拉伸试验测量得到460 MPa耐火钢室温泊松比为0.322，而拉扭试验测量计算材料室温的泊松比为0.335，误差仅为4%，验证了通过高温拉扭试验测量高温泊松比的可行性。
- 460 MPa耐火钢 /
- 高温拉伸与扭转 /
- 剪切模量 /
- 泊松比
Abstract: In order to measure Poisson's ratios for 460 MPa heat-resisting steel at high temperature, tension and torsion tests for 460 MPa heat-resisting steel at room temperature and high temperatures of 100 to 600℃ were completed on the MTS809 material testing machine. The elastic modulus and shear modulus of the material at different temperatures were measured with using high temperature tension-torsion extensometers. According to the relations between Poisson's ratio and the elastic formation modulus Poisson's ratios of steel at high temperatures were calculated. Poisson's ratios of 460 MPa heat-resisting steel at room temperature were 0.322 measured with radial and axial extensometers, while Poisson's ratios at room temperature were 0.335 measured and calculated in tension and torsion tests,and the error was 4%, which verificed the feasibility of Poisson's ratios measured in tension and torsion tests at high temperature.
- 460 MPa heat-resisting steel /
- tension and torsion at high temperature /
- shear modulus /
- Poisson's ratio