STUDY ON THE IMPACT OF CONCRETE CRACK SURFACE PRESSURE ON THE DEPTH TEST RESULTS
-
摘要: 在混凝土结构中，其应力状态随着荷载、温度等条件的不同会发生相应的变化。对混凝土结构中裂缝深度的无损检测，必须考虑裂缝面的应力状况，特别是深裂缝，其裂缝面上应力状况的影响则更加显著。利用大型混凝土块试验，比较在不同应力条件下，几种代表性的无损检测方法的测试结果。结果表明：当裂缝面上承受微小压应力时，相位反转法和传播时间差法均不能正确地测试裂缝深度；而当裂缝面上的压应力超过5 MPa时，现目前使用的检测方法都无法合理地测出裂缝的深度。因此，在检测裂缝深度时，需要密切关注裂缝面上的应力状态，同时，通过表面波法得到的裂缝深度测试结果的变化，间接地推测裂缝面上应力状态，为结构的分析提供相应依据。Abstract: In the concrete structure, the stress may change with load and tempercture etc.For crack depth testing by NDT methods, the stress condition of crack surface must be considered, especially for deep crack.In this paper, the results by large concrete block test were got.It was compared the difference between several representative nondestructive testing methods at the different stress conditions.The results show that the tested crack depth may be underestimated seriously by phase inversion methodand propagation time method, and the surface wave method performs better when the compressive stress on the crack surface is equal to, or less than 5 MPa.
-
Key words:
- concrete structure /
- crack depth /
- compressive stress /
- elastic wave /
- NDT /
- surface wave method
-
[2] 小林一辅．混凝土构造物的非破坏性检验[M].东京:森北出版株式会社,1996. 社团法人日本非破坏性检查协会．混凝土构造物的非破坏性试验法[M].东京:株式会社养贤堂,1994. [3] 英国标准协会．(BS 4408－5)混凝土非破坏性测试方法的建议．1974. [4] 呉佳曄,堤知明．コンクリートひび割れ深さの NDT 方法検証比較[C]∥弾性波法の非破壊検査研究小委員会報告書および第2回弾性波法によるコンクリートの非破壊検査に関するシンポジウム講演概要集．コンクリート技術シリーズ No．73,日本土木学会,2007. [5] 呉佳曄．コンクリート構造物のひび割れの深さ測定方法[C]∥弾性波法の非破壊検査研究小委員会報告書および第2回弾性波法によるコンクリートの非破壊検査に関するシンポジウム講演概要集．コンクリート技術シリーズ No．73,日本土木学会,2007. [6] 吴佳晔,安雪晖,田北平．混凝土无损检测技术的现状和进展[J].四川理工学院学报,2009,22(4):4－7. [7] 梁明进:钢筋混凝土结构裂缝深度无损检测技术的现状及发展[J].四川理工学院学报,2012,25(4):6－9. [8] 张霖波,王金枝,杨吉新．混凝土裂缝超声检测试验研究[J].武汉理工大学学报,2006.30(4): [9] 濮存亭．混凝土裂缝深度的声波衍射法检测技术研究与智能化裂缝深度测试仪[C]∥第十届全国建设工程无损检测技术学术会议论文集．中国土木工程学会,2008. [10] CECS 21∶2000超声法检测混凝土缺陷技术规程[S]. -
点击查看大图
计量
- 文章访问数: 104
- HTML全文浏览量: 7
- PDF下载量: 67
- 被引次数: 0
下载: