RESEARCH ON THE ANTI-CRACK BEARING CAPACITY OF STEEL REINFORCED HIGH-STRENGTH CONCRETE SHORT-LEG SHEAR WALL JOINTS
-
摘要: 为了研究型钢高强混凝土短肢剪力墙节点的抗裂能力,以配钢形式、轴压比和梁结构类型为变化参数设计了4个型钢高强混凝土短肢剪力墙节点试件和1个高强混凝土短肢剪力墙节点试件进行低周反复荷载试验,观察试件的受力破坏全过程,并获取其开裂荷载。结果表明:节点破坏先后经历初裂、通裂、极限和破坏4个阶段,开裂荷载约为极限荷载的30%～40%,配钢形式对节点抗裂承载力的影响较明显,增大轴压比对节点抗裂承载力有所提高。在试验基础上提出节点抗裂承载力计算公式,计算值与试验值吻合较好。Abstract: In order to research the anti-crack bearing capacity of steel reinforced high-strength concrete short-leg shear wall joint,4 steel reinforced high-strength concrete short-leg shear wall joints and 1 high-strength concrete short-leg shear wall joint are designed for the low cycle loading test,taking account of the variable parameters of steel type,axial compression ratio and beam type．Test results show that the whole failure process of joints experiences first-crack,full-crack, ultimate and failure successively.First-crack loading is approximately from 30 to 40 percentage of ultimate loading．Different steel type has the obvious influence on the anti-crack bearing capacity．Increasing axial compression ratio can improve the anti-crack bearing capacity of joints.Based on experimental research,the anti-crack bearing capacity formula of joint is proposed,calculated results agree well with test results．
-
李青宁，李晓蕾，闫艳伟，等．钢筋混凝土短肢剪力墙抗震性能试验研究[J].建筑结构学报，2011，32(4):53－62. [2] 周云，刘自力，刘丰，等．一字形短肢剪力墙抗震性能的模型试验研究[J].建筑结构学报，2008，29(4):81－88. [3] 黄东升．混凝土短肢剪力墙的理论分析与试验研究[D].南京:东南大学，2004. [4] 贾波.型钢高强混凝土T 型截面短肢剪力墙抗震性能试验研究[D].南宁: 广西大学，2009. [5] 伍依禄.型钢高强混凝土L 型截面短肢剪力墙正截面承载力研究[D].南宁: 广西大学，2011. [6] 凌湘.型钢高强混凝土T 型截面短肢剪力墙受力性能研究[D].南宁: 广西大学，2011. [7] 张磊，杨晓丽.型钢混凝土异型边节点承载力计算方法分析[J].工业建筑，2011，41(增刊): 297－301. [8] 赵鸿铁.钢与混凝土组合结构[M].北京: 科学出版社，2001. [9] 过镇海.钢筋混凝土原理和分析[M].北京: 清华大学出版社，2003. [10] 曾磊.型钢高强高性能混凝土框架节点抗震性能及设计计算理论研究[D].西安: 西安建筑科技大学，2008． -
点击查看大图
计量
- 文章访问数: 107
- HTML全文浏览量: 6
- PDF下载量: 68
- 被引次数: 0
下载: