Q460高强度焊接H型钢残余应力试验研究

童乐为,  赵俊,  周锋,  陈以一,  胡晓萍

downloadPDF
文章导航 > 工业建筑  > 2012 >  42(1): 51-55,17
童乐为, 赵俊, 周锋, 陈以一, 胡晓萍. Q460高强度焊接H型钢残余应力试验研究[J]. 工业建筑, 2012, 42(1): 51-55,17. doi: 10.13204/j.gyjz201201009
引用本文: 童乐为, 赵俊, 周锋, 陈以一, 胡晓萍. Q460高强度焊接H型钢残余应力试验研究[J]. 工业建筑, 2012, 42(1): 51-55,17. doi: 10.13204/j.gyjz201201009
shu
Tong Lewei, Zhao Jun, Zhou Feng, Chen Yiyi, Hu Xiaoping. EXPERIMENTAL INVESTIGATION ON LONGITUDINAL RESIDUAL STRESS OF Q460 HIGH-STRENGTH STEEL WELDED H-SECTION MEMBERS[J]. INDUSTRIAL CONSTRUCTION, 2012, 42(1): 51-55,17. doi: 10.13204/j.gyjz201201009
Citation: Tong Lewei, Zhao Jun, Zhou Feng, Chen Yiyi, Hu Xiaoping. EXPERIMENTAL INVESTIGATION ON LONGITUDINAL RESIDUAL STRESS OF Q460 HIGH-STRENGTH STEEL WELDED H-SECTION MEMBERS[J]. INDUSTRIAL CONSTRUCTION, 2012, 42(1): 51-55,17. doi: 10.13204/j.gyjz201201009
shu

Q460高强度焊接H型钢残余应力试验研究

doi: 10.13204/j.gyjz201201009
  • 1.

    1. 同济大学土木工程防灾国家重点实验室,上海 200092;

  • 2.

    2. 同济大学建筑工程系,上海 200092;

  • 3.

    3. 宝钢集团结构钢研究所,上海 201900

基金项目: 

科技部国家重点实验室基础研究资助项目(SLDRCE10-B-08);国863计划项目(2007AA03Z505)

详细信息
    作者简介:

    童乐为，男，1961年出生，博士，教授。E－mail:tonglw@tongji.edu.cn

EXPERIMENTAL INVESTIGATION ON LONGITUDINAL RESIDUAL STRESS OF Q460 HIGH-STRENGTH STEEL WELDED H-SECTION MEMBERS

  • 1.

    1. State Key Laboratory of Disaster Reduction in Civil Engineering,Tongji University,Shanghai 200092,China;

  • 2.

    2. Department of Building Engineering,Tongji University,Shanghai 200092,China;

  • 3.

    3. Research Institute of Structural Steel,Baosteel Group Corporation,Shanghai 201900,China

    摘要
  • 摘要: 针对宝钢最新研发的高强度Q460钢材,采用钻孔应变释放法测试焊接H型钢纵向残余应力在截面上的大小及分布规律。同时,结合机械剥层的方式对纵向残余应力沿壁厚方向的分布规律进行试验考察。在试验测试结果的基础上,提出高强度Q460焊接H型钢的纵向残余应力分布的计算模型。
    Abstract: It was presented an experimental investigation on longitudinal residual stresses of welded H-sections fabricated from high-strength steel sheet with a nominal yield stress of 460 MPa,which was recently developed by Baosteel Group Corporation.Strain gage hole drilling method was used to measure the magnitudes and distributions of longitudinal residual stresses along the cross section.Furthermore,the measured points inside the thickness were stripped to the outer surface to measure the stresses along the thickness of the section.At last,a longitudinal residual stress pattern was proposed based on the test results obtained in this study for the Q460 welded H-sections.
    • HTML全文
    • 参考文献(9)
  • 欧阳可庆. 钢结构[M].北京:中国建筑工业出版社,1995.
    文西芹,刘成文. 基于逆磁致伸缩效应的残余应力检测方法[J].传感器技术,2002,(03):42-44.
    Mather J. Determination of Initial Stresses by Measuring the Deformations Around Drilled Holes[J].Iron Steel Trans ASME,1934.249-254.
    American Society for Testing Material.E837-81,Standard Method for Determining Residual Stresses by the Hole-Drilling Strain-Gage Method[S].
    GB3395--1992残余应力测试方法钻孔应变释放法[S].
    施刚,王元清,石永久. 高强度钢材轴心受压构件的受力性能[J].建筑结构学报,2009,(02):92-97.
    何小东,张广成,裴怡. D406A高强钢焊接残余应力测试[J].焊接技术,2005,(02):50-51.
    Tebedge N,Alpsten G,Tall L. Residual-Stress Measurement by the Sectioning Method[J].Experimental Mechanics,1973,(13):88-96.
    Beg D,Hladnik L. Eigenspannungen bei Geschweissten I-Profilen Aus hochfesten Stahlen[J].Stahlbau,1994,(05):134-139.
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  106
  • HTML全文浏览量:  5
  • PDF下载量:  140
  • 被引次数: 0
出版历程
  • 收稿日期:  2011-06-25
  • 刊出日期:  2012-01-20

目录

    /

    返回文章
    返回

    期刊在线

    作者中心

    友情链接

    版权所有 ©《工业建筑》杂志社有限公司 京ICP备11033253号-1

    本系统由北京仁和汇智信息技术有限公司 设计开发   百度统计