再生混凝土抗冻耐久性试验研究

基金项目:

河南省科技攻关项目(编号:0124150)。

EXPERIMENTAL STUDY ON FROST-RESISTANT DURABILITY OF RECYCLED CONCRETE

1.
College of Enviroment and Water Conservancy Engineering,Zhengzhou University Zhengzhou 450002

摘要: 为了探讨再生骨料混凝土(RAC)的抗冻融耐久性能，选用三套配合比设计方案，即普通法、预湿水法和增浆法，通过冻融前后质量、动弹性模量和强度的对比研究，并与天然骨料混凝土(NAC)作对比。结果发现，加入引气剂后再生混凝土能达到甚至超过天然混凝土的抗冻性能，其中增浆法配制的再生混凝土的抗冻融性能最好；降低水灰比会提高抗冻性能；对于再生混凝土抗冻性能用质量损失和相对动弹性模量下降已经不能很好地衡量其抗冻性，引入强度损失这一指标更为合适。
- 再生混凝土 /
- 再生骨料 /
- 耐久性 /
- 冻融循环
Abstract: It is described a laboratory investigation on the resistance to freezing and thawing of recycled aggregate concrete (RAC).Comparing with the natural aggregate concrete (NAC) in the weight loss,the dynamic modulus of elasticity decrease and the strength,it is found that RAC is as durable as NAC.Especially,the durability of RAC by the design method of increasing cement paste is the most durable among the three kinds,even more durable than NAC.According to the result of the experiment,the strength reduction is used as the criterion of the freeze-thaw durability of RAC,besides the weight-loss and the decrease of dynamic modulus of elasticity.
- recycled concrete /
- regenerative aggregate /
- durability /
- freezing and thawing cycle

[2] 王武祥.拆除混凝土的再生试验研究.房材与应用,2001,29(5):19～21;

靳卫东,张弘强,戴文亭.关于回收混凝土再利用的研究.公路交通科技,2002,19(3):32～34;

[3] Mandal S,Chakarborty S,Gupta A.Some Studies on Durability of Recycled Aggregate Concrete.Indian Concrete Journal,2002,76(6):385～388;

[4] Salem,Rohi M.Resistance to Freezing and Thawing of Recycled Aggregate Concrete.ACI Materials Journal,2003,100(3):216～221;

[5] 王武祥.再生混凝土集料研究.混凝土与水泥制品,2001(4):9～12;

[6] 程红强,张雷顺,李平先.冻融对混凝土强度的影响.河南科学,2003,21(2):214～216

1.	陆春华，吴小龙，蔡启明，张菊连. 重复荷载作用后海工高性能混凝土梁刚度退化试验研究. 土木与环境工程学报(中英文). 2024(03): 171-179 . 百度学术
2.	谢生华，黄斌，周世康，龚明子，饶先鹏. 干湿循环与疲劳荷载耦合劣化作用下透水混凝土耐久性研究. 公路交通科技(应用技术版). 2020(02): 101-104 . 百度学术
3.	金珂宇，庞森，刁波，郑晓宁. 疲劳荷载幅值对氯环境下疲劳损伤RC梁剩余力学性能的影响. 混凝土. 2019(10): 1-4 . 百度学术