THE PREPARATION OF 150～200MPa SUPER HIGH STRENGTH & H IGH PERFORMANCE CONCRETE
-
摘要: 在分析活性粉末混凝土特点的基础上,研究了利用常规材料和普通工艺制备150～200MPa超高性能混凝土的可行性。研究结果表明,在不剔除粗集料的情况下,采用极低水胶比,配制出最高抗压强度达到170.3MPa的超高性能混凝土,混凝土拌合物的坍落度可以达到245mm,扩展度达到563mm。研究认为,为充分发挥混凝土成本低廉的优势,配制超高性能混凝土最佳的技术路径并不是剔除粗集料,而是如何去解决混凝土中由于粗集料所带来的缺陷问题。Abstract: In this paper,the authors analyze the character of the reactive powdered concrete.Using the ordinary materials a n d conventional technology,150～200MPa super high performance concrete with a slu mp245mm,spread563mm and 28d compressive strength170.3MPa has been success fully developed.Then the optimal economical technology for preparing super high performance concrete is using a coarse aggregate,whose key point is how to sett le the problem due to the course aggregate.
-
Key words:
- super high performance concrete /
- reactive powder concrete /
- coarse aggregate /
- strength /
- fluidity
-
[2] 蒲心诚,严吴南,王冲,等.100～150MPa超高强高性能混凝土的配制技术.混凝土,1 998(6) 蒲心诚,严吴南,王冲,等.150MPa超高强高性能混凝土研究与应用前景.混凝土,1999(3) [3] 覃维祖.活性粉末混凝土的研究.见:水泥基复合材料科学与技术--吴中伟院士从事科教工作60年学术讨论会论文集.北京:中国建材工业出版社,1999.33～35 [4] 陈兵,张东.新型水泥基复合材料的研究与应用.新型建筑材料,2000(4):28～ 30 [5] 朱英磊.活性粉末混凝土的性能研究及应用.混凝土,2000(7): 31～ 33 [6] 潘钢华.水泥基复合材料的组成结构和界面效应与强度关系的研究:[博士学位论文]. 南京:东南大学,1997.55～56 [7] 许仲梓.低孔隙率胶凝材料组成、结构和力学性能的关系及其改性研究:[博士学位论文].南京:南京化工学院,1988.22 -
点击查看大图
计量
- 文章访问数: 182
- HTML全文浏览量: 19
- PDF下载量: 178
- 被引次数: 0
下载: